ELAPLUS EP 1707A/B high temperature resistant two-component epoxy structural adhesive
EP 1707A/B epoxy adhesive is a resin adhesive that can be cured at room temperature/heating. This two-component adhesive is designed for metal bonding, bonding of cabin or SMC fiberglass components, splicing of aluminum honeycomb panels, and bonding of magnetic steel tiles for motor products, sealing of ceramic film components, bonding of internal structural adhesives for lithium battery modules, potting of soft magnetic units, and potting of high-temperature sensors.
- Color: Part A: Black; Part B: brownish yellow; Customizable colors
- Viscosity（25℃ mPa·s）：A Part：101,500±20,000；B Part：32,500±10,000； Mixed ratio：330,000±10000；
- Density（25℃ g/cm3）：A Part：1.28±0.05；B Part ：1.30±0.05；
Product Details
Feature
■ Resistance to moisture, dirt, and other atmospheric components
■ High strength, excellent adhesion
■ Good pollution resistance and low surface pretreatment requirements
■ No solvents, no curing by-products
■ Excellent resistance to high and low temperatures, -50 ℃ -180 ℃
■ Resistant to transformer oil, low attenuation
■ Good adhesion to fiberglass cloth, aluminum and plastic, aluminum and aluminum, and steel plates
Application
■ Metal bonding, shelter or SMC fiberglass component bonding
■ Aluminum honeycomb panel splicing and motor product magnetic steel tile bonding
■ Ceramic membrane component sealing
■ Internal structural adhesive bonding of lithium battery modules
■ Potting of soft magnetic units,Potting of high-temperature resistant sensors, etc
Product parameter
| Item | Unit | Standard | Typical value |
|---|---|---|---|
| Color | – | Visual inspection | A：White；B：Grey/White |
| Viscosity | mPa.s @RT 0.5rpm | GB/T 10247-2008 | A：180,000；B：220,000 |
| Density | 25℃，g/cmg/cm3 | GB/T 13354-92 | A：1.23±0.05；B：1.35±0.05 |
| Mix ratio | Ratio=A:B | Mass Ratio | 100：100 |
| Mixing Ratio | Ratio=A:B | Volume ratio | 100：100 |
| Mixing ratio | 25℃，mPa·s | GB/T 10247-2008 | 200,000 |
| Pot life | 25℃，100g，min | GB/T 10247-2008 | 50±10 |
| Hardness | Shore D | GB/T 531.1-2008 | 80±5 |
| T-shaped peel strength | N/mm(25℃) | GB/T2791-1995 | 6 |
| Impact strength | KJ/mg/cm2 | GB/T 1843-2008 | 15 |